PEMANFAATAN BIOMASSA SERAT KELAPA SAWIT DALAM PEMBUATAN BIOKOMPOSIT MAGNETIK NANOPARTIKEL SEBAGAI ADSORBEN PADA PENGOLAHAN LIMBAH CAIR SASIRANGAN

Gazaly, Ahmad and Karima, Ismi Nur and Nata, Iryanti Fatyasari PEMANFAATAN BIOMASSA SERAT KELAPA SAWIT DALAM PEMBUATAN BIOKOMPOSIT MAGNETIK NANOPARTIKEL SEBAGAI ADSORBEN PADA PENGOLAHAN LIMBAH CAIR SASIRANGAN. PEMANFAATAN BIOMASSA SERAT KELAPA SAWIT DALAM PEMBUATAN BIOKOMPOSIT MAGNETIK NANOPARTIKEL SEBAGAI ADSORBEN PADA PENGOLAHAN LIMBAH CAIR SASIRANGAN (SNIKSDA 2016).

[img]
Preview
Text
Binder21.pdf

Download (1308Kb) | Preview

Abstract

Abstrak- Serat kelapa sawit (fiber cake) adalah limbah pengolahan industri minyak kelapa sawit yang berpotensi sebagai sumber serat alami. Penelitian ini bertujuan memanfaatkan serat kelapa sawit untuk pembuatan biokomposit magnetik nanopartikel sebagai adsoben yang digunakan menurunkan kandungan logam timbal (Pb2+) dan Total Suspended Solid (TSS) limbah cair sasirangan. Biokomposit magnetik nanopartikel dibuat dengan sintesis solvothermal pada 198 oC selama 6 jam. Serat kelapa sawit yang sudah kering, dihaluskan, kemudian dilignifikasi untuk menghilangkan kadar lignin dengan 1% NaOH. Pada proses ini dihasilkan 2 jenis biokomposit tanpa amino grup (BSKS-M) dan dengan amino grup (BSKS-MH). Hasil pengamatan dari Scanning Electron Microscopy (SEM), magnetik nanopartikel telah terbentuk pada permukaan serat kelapa sawit. Treatment serat kelapa sawit dengan NaOH telah menstrukturisasi amorphous cellulose menjadi crystalline celloluse yang ditunjukkan kenaikan Crystalinity Index (CrI) sebesar 30,25% berdasarkan analisa X-Ray Diffraction (XRD). Kandungan Pb2+ yang diserap oleh BSKS-M dan BSKS-MH masing-masing pada 92,29 mg/g dan 100,10 mg/g selama 2 jam pada pH 6. Modifikasi amino grup pada permukaan biokomposit memberikan efek kenaikan adsorpsi sebesar 9%. Efektifitas penurunan TSS pada kondisi yang sama memberikan nilai sebesar 55,98% dan 45,70% untuk BSKS-M dan BSKS-MH. Kata kunci: Serat kelapa sawit, Adsorben, Biokomposit, Logam Pb2+, TSS Abstract- Palm fiber (fiber cake) is processing waste palm oil industry as a potential source of natural fiber. This research aims to use biocomposites fiber cake for the manufacture of magnetic nanoparticles as adsobent used to lower metal content of lead (Pb2+) and Total Suspended Solid (TSS) sasirangan liquid waste. Biocomposite magnetic nanoparticles prepared by solvothermal synthesis at 198 ° C for 6 hours. Oil palm fiber is dried, crushed, and then dilignifikasi to remove the lignin content with 1% NaOH. In this process produced two types of biocomposites without amino groups (BSKS-M) and the amino group (BSKS-MH). Observations of Scanning Electron Microscopy (SEM), magnetic nanoparticles have been formed on the surface of the fiber cake. Treatment with NaOH palm fiber was reconstructed amorphous crystalline cellulose into celloluse which shown by increasing Crystalinity Index (CRI) of 30.25% based on the analysis of X-Ray Diffraction (XRD). The content of Pb2+ absorbed by BSKS-M and BSKS-MH for 2 hours at pH 8 about 92.29 mg/g and 100.1 mg/g, respectively. Modification of amino groups on the surface biocomposite give rise adsorption effect of 9%. Effectiveness decrease of TSS on same condition at pH 6 for BSKS-M and BSKS-MH with a value of 55.98% and 45.7%. Keywords: oil palm fiber, Adsorbent, Biocomposites, Pb2+, TSS

Item Type: Article
Subjects: Q Science > QD Chemistry
Divisions: Fakultas Teknik > Teknik Kimia
Depositing User: Mr Arief Mirathan - Eka Setya Wijaya
Date Deposited: 01 Sep 2016 07:46
Last Modified: 06 Sep 2016 02:08
URI: http://eprints.unlam.ac.id/id/eprint/1206

Actions (login required)

View Item View Item